| Name︰ | high alumina cement |
| Country of Origin︰ | China |
|
|
|
| specifications︰ | HIGH ALUMINA REFRACTORY CEMENT
1. HIGH ALUMINA CEMENT A500
AL2O3:51%MIN FE2O3:3%MAX; SIO2:8% MAX CAO32%MIN
INITIAL SETTING TIME: 40 MINUTES MIN
FINAL SETTING TIME:10HR MAX
COMPRESSIVE STRENGTH:52Mpa AFTER 3DAYS
BENDING STRENGTH:5.5Mpa AFTER 3 DAYS
SIZE:90%MIN PASSING THROUGH 180MESH.
REFRACTORINESS:1450 ℃
PACKING: IN 25KG/BAG THEN 880 BAGS INTO CONTAINER
QUANTITY:20MT/LOT MIN AND 1500MT LOT MAX
2. HIGH ALUMINA CEMENT A600
AL2O3:53%MIN FE2O3:3%MAX; SIO2:8% MAX CAO32%MIN
INITIAL SETTING TIME: 40 MINUTES MIN
FINAL SETTING TIME:9HR MAX
COMPRESSIVE STRENGTH:62Mpa AFTER 3DAYS
BENDING STRENGTH:6.5Mpa AFTER 3 DAYS
SIZE:93 %MIN PASSING THROUGH 180MESH.
REFRACTORINESS:1450 ℃
PACKING: IN 25KG/BAG THEN 880 BAGS INTO CONTAINER
QUANTITY:20MT/LOT MIN AND 1500MT LOT MAX
3. HIGH ALUMINA CEMENT A700
AL2O3:53%MIN FE2O3:2.5%MAX; SIO2:7% MAX CAO33%MIN
INITIAL SETTING TIME: 40 MINUTES MIN
FINAL SETTING TIME:8HR MAX
COMPRESSIVE STRENGTH:72Mpa AFTER 3DAYS
BENDING STRENGTH:7.5Mpa AFTER 3 DAYS
SIZE:95%MIN PASSING THROUGH 180MESH.
REFRACTORINESS:1450 ℃
PACKING: IN 25KG/BAG THEN 880 BAGS INTO CONTAINER
QUANTITY:20MT/LOT MIN AND 1500MT LOT MAX
4. HIGH ALUMINA CEMENT A800
AL2O3:53%MIN FE2O3:2.5%MAX; SIO2:7% MAX CAO33%MIN
INITIAL SETTING TIME: 40 MINUTES MIN
FINAL SETTING TIME:8HR MAX
COMPRESSIVE STRENGTH:82Mpa AFTER 3DAYS
BENDING STRENGTH:8.5Mpa AFTER 3 DAYS
SIZE:95%MIN PASSING THROUGH 180MESH.
REFRACTORINESS:1450 ℃
PACKING: IN 25KG/BAG THEN 880 BAGS INTO CONTAINER
QUANTITY:20MT/LOT MIN AND 1500MT LOT MAX
REFERENCE PRICE:USD155/MT FOB CHINA MAIN PORT
5. HIGH ALUMINA CEMENT A900
AL2O3:53%MIN FE2O3:2.5%MAX; SIO2:7% MAX CAO33%MIN
INITIAL SETTING TIME: 40 MINUTES MIN
FINAL SETTING TIME:8HR MAX
COMPRESSIVE STRENGTH:92Mpa AFTER 3DAYS
BENDING STRENGTH:9.5Mpa AFTER 3 DAYS
SIZE:95%MIN PASSING THROUGH 180MESH.
REFRACTORINESS:1450 ℃
PACKING: IN 25KG/BAG THEN 880 BAGS INTO CONTAINER
QUANTITY:20MT/LOT MIN AND 1500MT LOT MAX
6.FUSED HIGH ALUMINA CEMENT
AL2O3:50%MIN FE2O3:1.5%MAX; SIO2:7% MAX CAO33%MIN
INITIAL SETTING TIME: 40 MINUTES MIN
FINAL SETTING TIME:4HR MAX
COMPRESSIVE STRENGTH:82Mpa AFTER 3DAYS
BENDING STRENGTH:8.5Mpa AFTER 3 DAYS
SIZE:95%MIN PASSING THROUGH 180MESH.
PACKING: IN 25KG/BAG THEN 880 BAGS INTO CONTAINER
QUANTITY:20MT/LOT MIN AND 200MT LOT MAX
|
|
|
|
|
|
|
|
|